Broad first-order magnetic entropy change curve in directionally solidified polycrystalline Ni-Co-Mn-In
Sánchez Llamazares, José Luis
Sánchez Valdés, Cesar Fidel
"We present the thermal dependence of the magnetic entropy change ΔSM(T) across the martensitic transformation for a polycrystalline sample, which was cut from a directionally solidified rod, with a nominal composition Ni42Co8Mn38In12 grown by the Bridgman-Stockbarger technique. This material combines a first-order martensitic transformation expanded over a very large working temperature range with a large magnetization change of ∼86 A m2 kg−1. Accordingly, for a magnetic field change of 5 T (2 T), the coupled magneto-structural transition gives rise to a broad magnetic entropy change curve across the reverse martensitic transformation with a moderate maximum value of 6.8 (3.0) J kg−1 K−1 and a full-width at half-maximum δTFWHM for the ΔSM(T) curve of 49 (43) K. Such a broad structural transition may be due to the effect of chemical segregation introduced by the directional solidification which can be enhanced by the non-uniform distribution of second phase particles. Accompanying with such a wide working temperature range, a large refrigerant capacity of 334 J kg−1 was obtained for a field change of 5 T."
Ferromagnetic shape memory alloy
Broad martensitic transformation
Working temperature range
CitationF. Chen, Y.X. Tong, L. Li, J.L. Sánchez Llamazares, C.F. Sánchez-Valdés, P. Müllner, Broad first-order magnetic entropy change curve in directionally solidified polycrystalline Ni-Co-Mn-In, Journal of Alloys and Compounds, Volume 727, 2017, Pages 603-609.
The following license files are associated with this item: