Síntesis y funcionalización de nanopartículas de carbono tipo cebollas para fabricación de supercapacitores

dc.contributor.authorSanchez Rodriguez, Cesar Eduardo
dc.contributor.otherBecerril, Ignacio
dc.contributor.otherCruz, Isidro
dc.contributor.otherEncinas, Armando
dc.date.accessioned2020-07-08T15:51:12Z
dc.date.available2020-07-08T15:51:12Z
dc.date.issued2020
dc.identifier.urihttp://hdl.handle.net/11627/5446
dc.description.abstract"Por medio de la combustión de naftaleno se sintetizaron nanopartículas de car- bono tipo cebollas (CNOs), sin la presencia de un catalizador, produciéndose además grandes cantidades (a escala de gramos) en tiempos reducidos (en minu- tos). Las nanopartículas fueron tratadas químicamente (HNO3 y H2SO4 a diferen- tes concentraciones) para su funcionalización, posterior a este proceso se realizó un tratamiento térmico lo que incremento su porosidad y como resultado, un au- mento de su área superficial específica, a la vez que se mantuvo una buena grafi- tización. Imágenes obtenidas por la técnica de microscopía electrónica mostraron la formación de CNOs con un diámetro promedio de 35 nm; así como la presencia de capas grafíticas internas. Espectros de FT-IR mostraron que hubo efectivamen- te una funcionalización de las CNOs al ser sometidas a un baño de mezcla de áci- dos. Mientras que, espectros de Raman indicaron un incremento en la grafitización de las muestras, después de recibir el tratamiento térmico. Estas estructuras trata- das térmicamente mostraron un área superficial de ⁓300 m2/g. En este trabajo de tesis, sólo las muestras que recibieron el tratamiento térmico fueron preparadas para medir su capacitancia en una celda electrolítica con un arreglo de 3 electro- dos, donde se empleó 1M H2SO4 como electrolito, a diferentes velocidades de ba- rrido. Las muestras sometidas a un baño ácido y luego tratadas con un recocido térmico a 800°C mostraron una capacitancia específica de ⁓70 F/g a una velocidad de barrido de 5 mV/s; mientras que la muestra que sólo recibió recocido tér- mico final alcanzó un valor de 20.5 F/g."es_MX
dc.description.abstract"Through the combustion of naphthalene, onion-type carbon nanoparticles (CNOs) were synthesized, without the presence of a catalyst, and large quantities (on a gram scale) were also produced in reduced times (in minutes). The nanoparticles were chemically treated (HNO3 and H2SO4 at different concentrations) for their functionalization, after this process a thermal treatment was carried out which in- creased their porosity and as a result, an increase in their specific surface area, at the same time a good graphitization was maintained. Images obtained by the elec- tron microscopy technique showed the formation of CNOs with an average diame- ter of 35 nm; as well as the presence of internal graphite layers. FT-IR spectra showed that there was indeed a functionalization of the CNOs when subjected to an acid mixture bath. While Raman spectra indicated an increase in the graphitiza- tion of the samples, after receiving the heat treatment. These heat-treated struc- tures showed a surface area of ⁓300 m2/g. In this thesis work, only the samples that received the heat treatment were prepared to measure their capacitance in an electrolytic cell with a 3-electrode array, where 1M H2SO4 was used as the electro- lyte, at different scanning speeds. The samples subjected to an acid bath and then treated with a thermal anneal at 800°C showed a specific capacitance of ⁓70 F/g at a sweep speed of 5 mV/s; while the sample that only received final thermal an- nealing reached a value of 20.5 F/g."es_MX
dc.language.isospaes_MX
dc.rightsAtribución 4.0 Internacional*
dc.rights.urihttp://creativecommons.org/licenses/by/4.0/*
dc.subjectNanocebollas de carbonoes_MX
dc.subjectFuncionalizaciónes_MX
dc.subjectSupercapacitoreses_MX
dc.subject.classificationNanotecnología y materiales avanzadoses_MX
dc.subject.classificationArea::BIOLOGÍA Y QUÍMICA::QUÍMICAes_MX
dc.titleSíntesis y funcionalización de nanopartículas de carbono tipo cebollas para fabricación de supercapacitoreses_MX
dc.typemasterThesises_MX
dc.contributor.directorLópez Sandoval, Román
dc.contributor.directorReyes Reyes, Marisol
dc.audiencestudentses_MX


Files in this item

Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record

Atribución 4.0 Internacional
Except where otherwise noted, this item's license is described as Atribución 4.0 Internacional